Comparison of Microleakage and Shear Bond Strength of Ribbon and Twisted Wire Retainers Bonded on Human Mandibular Incisors With Two Different Types of Adhesives With and Without Primer: An In-Vitro Study Publisher Pubmed



Kavousinejad S1 ; Hosseinzadeh Nik T2 ; Saffar Shahroudi A2
Authors
Show Affiliations
Authors Affiliations
  1. 1. Department of Orthodontics, Tehran University of Medical Sciences, Tehran, Iran
  2. 2. Department of Orthodontics, Dental Research Center, Dentistry Research Institute, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran

Source: International Orthodontics Published:2022


Abstract

Background and objectives: Shear bond strength and microleakage are the success factors of fixed retainers. Recently, primer-free composites were introduced to reduce chair time. The main objectives of this study were to compare the shear bond strength (SBS) and microleakage of GC Ortho ConnectTM Flow (OF) and TransbondTM XT (TXT) with two types of common retainer wires (0.0175-inch twisted wire and 0.028 ×. 0.008-inch ribbon dead soft wire retainers). The secondary objectives of the study were to compare enamel-adhesive interface and wire-adhesive interface microleakages. Materials and methods: This in vitro study was conducted on 132 human mandibular incisors (96 for bond strength and 36 for microleakage). The teeth were randomly divided into four groups for use of ribbon and twisted wires with OF and TXT adhesives. The bond strength was measured by a universal testing machine. Microleakage was evaluated by the dye penetration test using 0.05% fuchsine. Data were analysed by two-way ANOVA (alpha = 0.05). Results: No significant difference was noted in bond strength among the four groups (P > 0.05). However, the microleakage of OF was significantly higher than that of TXT at both the enamel-adhesive and wire-adhesive interfaces (P < 0.001). The microleakage at the wire-adhesive and enamel-adhesive interface was not significantly different in groups 1 and 4 and was significant in group 2 and 3. Conclusion: Type of adhesive significantly affected the microleakage, and OF resulted in higher microleakage than TXT at both the enamel-adhesive and wire-adhesive interfaces. Type of wire had no significant effect on microleakage. Although OF showed comparable SBS to TXT, its higher microleakage may compromise its successful long-term clinical service. © 2022