A Modified Tegdma-Based Resin Infiltrant Using Polyurethane Acrylate Oligomer and Remineralising Nano-Fillers With Improved Physical Properties and Remineralisation Potential Publisher



Hashemian A¹ ; Shahabi S¹ ; Behroozibakhsh M¹ ; Najafi F² ; Abdulrazzaq Jerri Albakhakh B³ ; Hajizamani H¹ Show Affiliations
Source: Journal of Dentistry Published:2021

Abstract

Objectives: This study aimed to modify an experimental triethylene glycol dimethacrylate (TEGDMA) based resin infiltrant using PUA oligomer and two remineralising fillers, including fluorohydroxyapatite (FHA) and fluoride-doped bioactive glass (FD-BG), to improve the mechanical and physical properties and induce remineralising potential. Materials and methods: The polyurethane acrylate oligomer (PUA) was synthesised and characterised. Experimental resin infiltrant was prepared by mixing 10% of synthesised PUA with 88% TEGDMA. Water contact angle, penetration coefficient, and penetration depth were then measured. The FHA and FD-BG fillers were synthesised and characterised. To prepare nano-filled resin infiltrant, 5% of each powder was mixed with the prepared resin infiltrant. The prepared resin infiltrants were characterised to evaluate their degree of conversion, mechanical properties, water sorption, and solubility. The ion release of filled resin was also assessed. The non-infiltrated and infiltrated enamel specimens underwent fourteen days of pH-cycling, and a surface microhardness was done to assess the resistance to demineralisation. Results: The results showed that the addition of PUA to TEGDMA increased the mechanical properties and decreased water sorption and solubility. The addition of synthesised FD-BG fillers to resin infiltrant significantly improved the resistance to demineralisation of enamel samples compared with other groups (p ≤ 0.001). The FHA fillers also improved the resistance to demineralisation; however, the produced changes were not statistically meaningful (p > 0.05). Conclusions: Based on the results, the PUA+TEGDMA+ FD-BG/FHA composite can be used as an alternative material for pure TEGDMA in enamel infiltration approaches owing to its better mechanical properties, lower water sorption and solubility, and also remineralisation potential. Clinical Significance: A resin infiltrant with remineralisation potential, lower water sorption and solubility and higher mechanical properties may enhance the management of early caries lesions. © 2021