Surface Microhardness of Different Thicknesses of a Premixed Bioceramic Material With or Without the Application of a Moist Cotton Pellet Publisher



Shokouhinejad N¹ ; Razmi H¹ ; Khoshkhounejad M¹ ; Javani A² ; Raoof M³ Show Affiliations
Source: Dental Research Journal Published:2016

Abstract

Background: This study was conducted to assess the effect of thickness and hydration condition on the surface microhardness of Endosequence Root Repair Material putty (ERRM; Brasseler USA, Savannah, GA), a premixed bioceramic material. Materials and Methods: Polymethyl methacrylate cylindrical molds with an internal diameter of 4 mm and three heights of 2, 4, and 6 mm were fabricated. In Group 1 (dry condition), the molds with heights of 2, 4, and 6 mm (10 molds of each) were filled with ERRM. In Groups 2 and 3 (wet condition), a distilled water- or phosphate-buffered saline (PBS)-moistened cotton pellet was placed directly on the upper surface of ERRM, respectively. The lower surface of ERRM was in contact with floral foams soaked with human blood. After 4 days, Vickers microhardness of the upper surface of ERRM was tested. The data were analyzed using two-way analysis of variance. Significance level was set at P < 0.05. Results: No significant difference was found between the microhardness of three thicknesses of ERRM (2, 4, and 6 mm) with or without placing a distilled water- or PBS-moistened cotton pellet over the material (P > 0.05). Conclusion: Based on the results of this study, it could be concluded that placing a moistened cotton pellet on ERRM putty up to 6 mm thick might be unnecessary to improve its surface microhardness and hydration characteristics. © 2015 Dental Research Journal | Published by Wolters Kluwer - Medknow.