Comparative Evaluation of Fiber-Reinforced, Bulk-Fill and Conventional Dental Composites: Physical Characteristics and Polymerization Properties Publisher Pubmed



Pedram P1 ; Jafarnia S2 ; Shahabi S1, 3 ; Saberi S3 ; Hajizamani H1
Authors
Show Affiliations
Authors Affiliations
  1. 1. Department of Dental Biomaterials, School of Dentistry, Tehran University of Medical Sciences, Iran
  2. 2. Department of Dental and Biomedical Materials Science, Graduate School of Biomedical Sciences, Nagasaki University, Japan
  3. 3. Laser Research Center, Dentistry Research Institute, Tehran University of Medical Sciences, Iran

Source: Polimery w medycynie Published:2022


Abstract

BACKGROUND: Resin composites have various applications. At the same time, they have some drawbacks, such as polymerization shrinkage. Conventional composites are polymerized in 2-mm thick layers. However, in posterior restoration, the 2-mm depth of cure is not satisfactory. To find a solution, resin composites have been vastly improved in terms of fillers, matrix and initiators. OBJECTIVES: To evaluate polymerization properties and physical characteristics of fiber-reinforced composites and compare them with bulk-fill composites that are designed for large posterior restorations. MATERIAL AND METHODS: Samples were prepared from each resin composite. The 3-point bending test was performed to evaluate the flexural strength of all composites. The depth of cure of the composite from 1 mm to 4 mm of depth was analyzed using Vickers hardness test (VHN). To analyze the degree of conversion, Fourier-transform infrared spectroscopy (FTIR) of the top and bottom surfaces of the samples with 4-mm thickness was calculated. The data were analyzed using one-way analysis of variance (ANOVA) test followed by post hoc test (95% confidence interval (95% CI)). RESULTS: The Filtek showed the highest flexural strength followed by everX and X-tra fil. At 1-mm depth, X-tra fil had the highest and Gradia had the lowest microhardness. At the 4-mm depth, the microhardness trend was as follows: everX > Filtek > X-tra fil > Gradia > Beautifil. The everX composite had the lowest reduction of the degree of conversion at 4-mm thickness, which showed a significant difference in comparison with Filtek, Gradia and X-tra fil composites. CONCLUSIONS: Based on the results of our study, it can be concluded that the fiber-reinforced composite everX showed more favorable results regarding polymerization properties, such as the degree of conversion and the depth of cure. However, the flexural strength results in Filtek were better than those in everX.