Antimicrobial Properties, Anti-Virulence Activities, and Physico-Mechanical Characteristics of Orthodontic Adhesive Containing C-Phycocyanin: A Promising Application of Natural Products; [Антимикробные Свойства, Антивирулентная Активность И Физико-Механические Характеристики Ортодонтического Клея, Содержащего С-Фикоцианин: Перспективное Применение Натуральных Продуктов] Publisher Pubmed



Pourhajibagher M¹ ; Bahador A² Show Affiliations
Source: Folia Medica Published:2021

Abstract

Introduction: Antimicrobial orthodontic adhesives aim to reduce enamel demineralization, white spot lesions, and incipient tooth decay around bonded orthodontic brackets, but they should not imperil its mechanical properties. Aim: To evaluate the antimicrobial and physico-mechanical properties of acrylic containing different concentrations of C-phycocyanin on Streptococcus mutans, Lactobacillus acidophilus, and Candida albicans. Materials and methods: The mechanical properties of acrylic resins were measured by flexural strength test after preparation of acrylic resin samples with concentrations of 1%, 2%, 5%, 7.5%, and 10% of C-phycocyanin. Then we evaluated the antimicrobial effects of acrylic resin containing the maximum concentration of C-phycocyanin with clinically acceptable flexural strength and the changes in expression of virulence factors. Results: The highest and lowest means of flexural strength were obtained in acrylic resins containing 0% and 10% concentrations of C-phycocyanin at 50.2±4.5 and 30.1±3.3 MPa, respectively. Adding 1%, 2%, and 5% of C-phycocyanin showed no significant decrease in flexural strength (p>0.05). The maximum mean diameter of the growth inhibition zone was observed around discs containing 5% of C-phycocyanin. Until day 30 of the study, no microbial biofilms were formed on any acrylic disc. Only microbial biofilms of C. albicans were able to form on discs containing 5% of C-phycocyanin at 90 days. 5% C-phycocyanin could significantly decrease the expression levels of gtfB, hsp16, and ALS9 6.1-, 7.3-, and 3.9-fold, respectively. Conclusions: It can be concluded that the most acceptable concentration of C-phycocyanin in acrylic resin is 5% based on the results of flexural strength tests and antimicrobial activities of acrylic resin containing various concentrations of C-phycocyanin. © 2023 Folia Medica. All rights reserved.