Fracture Resistance of Three Different Posts in Restoration of Severely Damaged Primary Anterior Teeth: An in Vitro Study Publisher



Seraj B1 ; Ghadimi S2 ; Estaki Z3 ; Fatemi M4
Authors
Show Affiliations
Authors Affiliations
  1. 1. Dental Research Center, Dentistry Research Institute, Department of Pediatric Dentistry, Tehran, Iran
  2. 2. Laser Research Center of Dentistry, Department of Pediatric Dentistry, Tehran University of Medical Sciences, Tehran, Iran
  3. 3. Department of Pediatric Dentistry, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran
  4. 4. Department of Dental Biomaterials, Research Center for Science and Technology in Medicine, Tehran University of Medical Sciences, Tehran, Iran

Source: Dental Research Journal Published:2015


Abstract

Background: Restoration of anterior primary teeth with severe caries lesion is a big challenge. The aim of this study was to compare the fracture resistance of three types of post, including composite resin, customized quartz fiber and prefabricated glass fiber in restoration of severely damaged primary anterior teeth. Materials and Methods: Sixty extracted human primary maxillary incisors were randomly divided into three groups: Group 1: Customized quartz fiber post, Group 2: Composite post and Group 3: Prefabricated glass fiber post. Due to the effect of bonded area on the fracture resistance, the bonded surface of each sample was measured 1 mm above cementoenamel junction. An increasing force was subjected with a crosshead speed of 0.5 mm/min by a universal testing machine until fracture occurred, and the failure mode was assessed afterwards. Data were analyzed using One-way analysis of variance and Kruskal-Wallis tests. The level of significance was considered at P < 0.05. Results: The mean fracture resistance values of three groups were 343.28 N, 278.70 N and 284.76 N, respectively. Although customized quartz fiber post showed the greatest fracture resistance, statistical analysis revealed no significant difference between groups (P = 0.21). The mean fracture strength values of three groups were 12.82 N/mm-2 , 11.93 N/mm-2 and 11.31 N/mm-2 , respectively; however, the differences were not statistically significant (P = 0.72). Favorable failure mode was more frequent in all groups (P = 0.12). Conclusion: Within the limitations of this study, it can be concluded that all three types of studied posts can be successfully used to restore badly destructed primary anterior teeth.