Comparison of Marginal and Internal Adaptation in Endocrowns Milled From Translucent Zirconia and Zirconium Lithium Silicate Publisher



Amini A^{1, 2} ; Zeighami S^{1, 2} ; Ghodsi S^{1, 2} Show Affiliations
Source: International Journal of Dentistry Published:2021

Abstract

Purpose. This study aimed to compare marginal and internal adaptation in endocrowns made from translucent zirconia and zirconium lithium silicate using CAD-CAM technology. Materials and Methods. Twenty-eight freshly extracted upper molars were mounted in acrylic resin and underwent root canal therapy and endocrown preparation up to 2 mm above the cementoenamel junction. Endocrowns were CAD-CAM milled from zirconium lithium silicate (ZLS) and translucent zirconia (Zr). Internal and marginal adaptation was assessed by the replica technique before cementation. Marginal adaptation was evaluated by a stereomicroscope (×32) before and after cementation and also after thermomechanical aging. Results. The ZLS group showed significantly higher internal adaptation compared to the Zr group (P = 0.028), while the marginal adaptation differences, at different times with different methods, were not statistically significant (P > 0.05). Axiomarginal angle had the highest and axiopulpal angle showed the lowest adaptation in both groups. The cementation process and thermomechanical aging increased the marginal gap in both groups significantly (P < 0.001). The marginal gap assessed by the replica technique before cementation was 7.11 μm higher than direct view under a stereomicroscope with intraclass correlation coefficient of 0.797. Conclusion. Zirconia seems to be an acceptable material for endocrown with comparable internal and marginal adaptation to ZLS. Cementation and thermomechanical aging had significantly negative effects on marginal gap. The marginal gap assessed by the replica technique was higher than direct view under the stereomicroscope technique. © 2021 Amirhesam Amini et al.